Kaolin Noodle : [CN-83]
| Physical Property | Chemical Analysis | ||
| Shirinkage | 5.07% | SiO2 | 47.34% |
| Loss of ignition | 15.24% | AI2O3 | 36.97% |
| Dry MOR Kg/cm2 | Lamination | Fe2O3 | 0.28% |
| Fired MOR Kg/cm2 | 54.0% | TiO2 | 0.49% |
| Water Absoration | 20.84% | CaO | 0.27% |
| Water of plasticity | 36-38 | MgO | 0.45% |
| pH | 4-5 | K2O | 0.008% |
| Residue | 0.40% | Na2O | 0.1% |
| L* | 94.71 | Loss of ignition | 13.60% |
| A* | 0.42 | ||
| B* | 3.26 | ||
| Whitness | 88.78% | ||
| Temperature C. | 1220/1230 | ||
| Cycle Min | 55 | ||
Kaolin Noodles the properties includes
- High Suspension Property
- Low Shrink & Swell Capacity
- Increasing the firing range of the glaze
- Stiffen and melt the glaze effectively
- High Color performance